Material: 6000 Series
Annealing: O-H112
Species: Coil, Plate
Surface Treatment: Coated
Whether Alloy: Is Alloy
Place Of Origin: China
Tolerance: ±1%
Processing Service: Bending, Decoiling, Welding, Punching, Cutting
Color: Silver
Application: Transportation Tools, Door & Window, Glass Wall, Heat Sink, Decorations
Technique: Cold Drawn
Surface: Mill Finish/Mirror Finish
Width: 200mm-2600mm
Length: 6000mm or as Customer′s Requirement
Selling Units | : | Ton |
Package Type | : | Standard Export Packing |
Picture Example | : |
The file is encrypted. Please fill in the following information to continue accessing it
6000 series Aluminum plate is commonly used in aircraft parts, camera parts, couplers, marine accessories and hardware, electronic accessories and joints, etc.
6063 is an Aluminium alloy, with magnesium and silicon as the alloying elements. The standard controlling its composition is maintained by The Aluminum Association. It has generally good mechanical properties and is heat treatable and weldable. It is similar to the British aluminium alloy HE9.
6063 is the most common alloy used for aluminium extrusion. It allows complex shapes to be formed with very smooth surfaces fit for anodizing and so is popular for visible architectural applications such as window frames, door frames, roofs, and sign frames. Applications requiring higher strength typically use 6061 or 6082 instead.
No. | Alloy States | ||||||||||||||||
Chemical composition.% | |||||||||||||||||
Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn |
| Ti | Zr | Other | AI | |||||
| Single | Total | |||||||||||||||
1 | 3003 | 0.6 | 0.7 | 0.05-0.20 | 1.0-1.5 | - | - | - | 0.1 | - | - | - | 0.05 | 0.15 | Rem | - | |
2 | 4032 | 11.0-13.5 | 1 | 0.50-1.30 | - | 0.8-1.3 | 0.1 | 0.50-1.30 | 0.25 | - | - | - | 0.05 | 0.15 | Rem | - | |
3 | 4043 | 4.5-6.0 | 0.8 | 0.3 | 0.05 | 0.05 | - | - | 0.1 | - | 0.2 | - | 0.05 | 0.15 | Rem | - | |
4 | 4047 | 11.0-13.0 | 0.8 | 0.3 | 0.15 | 0.1 | - | - | 0.2 | - | - | - | 0.05 | 0.15 | Rem | - | |
5 | 5052 | 0.25 | 0.4 | 0.1 | 0.1 | 2.2-2.8 | 0.15-0.35 | - | 0.1 | - | - | - | 0.05 | 0.15 | Rem | - | |
6 | 5754 | 0.4 | 0.4 | 0.1 | 0.5 | 2.6-3.6 | 0.3 | - | 0.2 | Mn+Cr:0.1-0.6 | 0.15 | - | 0.05 | 0.15 | Rem | - | |
7 | 5182 | 0.2 | 0.35 | 0.15 | 0.20-0.50 | 4.0-5.0 | 0.1 | - | 0.25 | - | 0.1 | - | 0.05 | 0.15 | Rem | - | |
8 | 5083 | 0.4 | 0.4 | 0.1 | 0.40-1.0 | 4.0-4.9 | 0.05-0.25 | - | 0.25 | - | 0.15 | - | 0.05 | 0.15 | Rem | LF4 | |
9 | 6061 | 0.40-0.8 | 0.7 | 0.15-0.40 | 0.15 | 0.8-1.2 | 0.04-0.35 | - | 0.25 | - | 0.15 | - | 0.05 | 0.15 | Rem | LD30 |
Alloy States | Thickness (mm) | Tensile strenght (Rm/Mpa) | Yield Strength (Rp0.2 Mpa) | Elongation A50(%) | Bending Radius |
5052 H32 | >0.20-0.50 | 210-260 | 130 | 5 | 0.5t |
>0.50-1.50 | 6 | 1.0t | |||
>1.50-3.00 | 7 | 1.5t | |||
>3.00-6.00 | 10 | 1.5t | |||
5052 H34 | >0.20-0.50 | 230-280 | 150 | 4 | 0.5t |
>0.50-1.50 | 5 | 1.5t | |||
>1.50-3.00 | 6 | 2.0t | |||
>3.00-6.00 | 7 | 2.5t | |||
5052 H36 | >0.20-0.50 | 250-300 | 180 | 3 | 1.5t |
>0.50-1.50 | 4 | 2.0t | |||
>1.50-3.00 | 5 | 3.0t | |||
>3.00-6.00 | 6 | 3.5t | |||
5052 H38 | >0.20-0.50 | 270 | 210 | 3 | - |
>0.50-1.50 | 3 | - | |||
>1.50-3.00 | 4 | - |